HandiFoam System 120 Refill Low Pressure Polyurethane Spray Foam Insulation P23490

Low pressure, medium density, two-component spray polyurethane foam.

• Designed to fill and seal various size voids, deaden sound or reduce vibration
• Conforms to the requirements of ASTM E84 as a Class 1 (A) system

Substrate must be clean, dry, firm, free of loose particles, and free of dust, grease, and mold release agents. Protect surfaces not to be foamed. Read SDS, Operating Instructions, and Product Stewardship Guidelines.

Condition chemical to 75-85°F (24-29°C). Follow instructions for set-up found in the operating instructions.

Recommend using in a well-ventilated area with certified respiratory protection or a powered air purifying respirator (PAPR). Wear protective glasses with side shields or goggles, nitrile gloves, and clothing that protects against dermal exposure.

FOR PROFESSIONAL USE ONLY. Always check the local building code before use. Cured low-pressure polyurethane foam is non-toxic and inert.

Store in a dry area. Do not expose the kits or tanks to open flame or temperatures above 90°F (32°C). Excessive heat can cause premature aging of components resulting in a shorter shelf-life.

Always dispose of empty cylinders according to applicable federal, state, provincial, and local regulations.

6 months

Cured low-pressure polyurethane foam is chemically inert and non-reactive in approved applications and will not harm electrical wire insulations, extruded polystyrene foams, Romex®, rubber, PVC, polyethylene (i.e. PEX), or other plastics. The product is not resistant to UV rays; if left exposed, it should be coated or painted.

• Product Type: Spray Foam Insulation
• Chemical Storage Temperature: Optimum 75-85°F (24-29°C), but not <60°F (16°C) or >90°F (32°C)
• Outside Application Temperature: 40-100°F (4-38°C)
• Process Core Chemical Temperature: 75-85°F (24-29°C)
• Surface Temperature (Substrate): 40-100°F (4-38°C)
• Cured Foam Temperature Range: -200 to +240°F (-129 to +116°C)
• Density Free Rise: ASTM D1622 - 2.0 lbs/ft³ (32.0 kg/m³)
• Density In-place: 2.3 lbs/ft³ (36.8 kg/m³)
• K-factor - Initial: ASTM C518 - 0.154 BTU∙inch/ft²∙h∙°F at 1” thickness
• K-factor - Aged 90 days 140°F (60°C): ASTM C518 - 0.163 BTU∙inch/ft²∙h∙°F at 1” thickness
• R-Value - Initial: ASTM C518 - 6.50 at 1” thickness
• R-Value - Aged 90 days 140°F (60°C): ASTM C518 - 6.10 at 1” thickness
• Air Barrier Properties (Tested at 1” thickness @1.57 psf (75Pa)): ASTM E283 - 0.003 cfm/ft² (0.02 L/s/m²)
• Air Permeance (Tested at 0.5” bead @1.57 psf (75Pa)): ASTM E2178 - 0.002 cfm/ft² (0.01 L/s/m²)
• Compressive Strength: ASTM D1621 - 20 lbf/in² (138 kPa) Parallel, 18 lbf/in² (124 kPa) Perpendicular
• Dimensional Stability:
  • 70°F (22°C) & 50% R.H. / 30 days: +/- 5%
  • -4°F (-20°C) / 30 days: + 0.2%
  • 158°F (70°C) & 97% R.H. / 30 days: + 9.7%
• Shelf-life: 6-Months
• Tack-Free/Expansion Time: 45-75 seconds
• Closed-Cell Content: ASTM D2856 - 92%
• Tensile Strength: ASTM D1623 - 32 lbf/in² (221 kPa) Parallel
• Cuttable: ~5 minutes (estimate)
• Fungi Resistance: ASTM G21 - No Growth
• Perm Rating - Method A (1” Thick (2.54 cm)): ASTM E96 - 1.6 perms - Class III Vapor Retarder
• VOC Content: EPA Method 24 - <25 g/L (minus water and exempt compounds)
• Fire Rating (Tested at 3” Thickness): ASTM E84 - Flame Spread Index 10, Smoke Developed 450
• Fire Rating (Tested at 4” Beads): CAN/ULC S102 - Flame Spread Index 15, Smoke Developed 225
• Fire Rating: FMVSS 302/CMVSS 302 - Meets/Burn Rate 0/00 min
• Size: 60G
• Board Feet: 6,816 bdft
• Cubic Feet: 568 cu. ft.
• Linear Feet: 104,140 ft at 1 inch Bead
• Weight²(Per Cylinder): 705 lbs